| PA6 1030 日本三菱化成工业公司 物性数据 |
| 规格级别： | 挤压级 | 外观颜色： | --- |
| 用途概述： | 特别适合于风冷吹气成型 | ||
| 备注说明： | 特性：高粘度，透明度高 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||||||||
| 基本性能 | 吸水率 | 65%湿度 | ASTM D-570 | 3.5 | % | |||||||||
| 物理性能 | 比重 | --- | ASTM D-792 | 1.14 | --- | |||||||||
| 塔伯磨损 | --- | ASTM D-256 | 7 | mg/1000cycles | ||||||||||
| 摩擦系数 | --- | ASTM D-785 | 0.14 | --- | ||||||||||
| 机械性能 | 弯曲模量 | --- | ASTM D-256 | 2.55(9.51) | GPa(104Kgf/cm2) | |||||||||
| IZOD冲击强度 | --- | ASTM D-790 | 49(740) | J/m(kgf.cm/cm) | ||||||||||
| IZOD冲击强度 | 1/8 | ASTM D-790 | 64(88) | J/m(kgf.cm/cm) | ||||||||||
| 洛氏硬度 | --- | ASTM D-256 | 120（85） | R Scale | ||||||||||
| 拉伸强度 | --- | ASTM D-638 | 76.4(37.2) | MPa(Kgf/cm2) | ||||||||||
| 拉伸长度 | --- | ASTM D-638 | ＞200 | % | ||||||||||
| 挠曲强度 | --- | ASTM D-790 | 98.1(47.0) | MPa(Kgf/cm2) | ||||||||||
| 电气性能 | 体积电阻系数 | --- | ASTM D-1044 | 1015(1012) | --- | |||||||||
| 解电压 | --- | ASTM D-1894 | 20(12-15) | MV/m | ||||||||||
| 介电常数 | --- | ASTM D-150 | 35-44(132) | Pf/m | ||||||||||
| 介电耗损正切 | --- | ASTM D-150 | 0.03(0.1) | --- | ||||||||||
| 电弧电阻系数 | --- | ASTM D-495 | 180-190 | S | ||||||||||
| 加工性能 |
|
|
--- |
|
|
|||||||||
| 热 性 能 | 线膨胀系数 | --- | ASTM D-696 | 9 | 10-5.k-1 | |||||||||
| 负荷挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 160 | ℃ | ||||||||||
| 负荷挠曲温度 | 18.6kgf/cm2 | ASTM D-648 | 64 | ℃ | ||||||||||