②原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
frame="void">
| 测试数据 |
| DAM |
50%RH |
|
数据单位 |
| 基本性能 |
吸水率 |
24小时浸渍(23℃) |
ASTM D-570 |
|
% |
| 吸水率 |
饱和(23℃) |
ASTM D-570 |
|
% |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
|
--- |
| 泰伯磨耗量 |
cs-17 Wheel,1000g |
--- |
|
mg/1000 cycles |
| 机械性能 |
硬度计硬度 |
--- |
ASTM D-676 |
|
--- |
| 洛氏硬度M |
--- |
ASTM D-785 |
|
--- |
| 洛氏硬度R |
--- |
ASTM D-785 |
|
--- |
| 拉伸强度 |
23℃ |
ASTM D-638 |
|
MPa |
| 屈服强度 |
23℃ |
--- |
|
MPa |
| 断裂伸长率 |
23℃ |
ASTM D-638 |
|
% |
| 屈服伸长率 |
--- |
ASTM D-638 |
|
% |
| 剪切强度 |
23℃ |
ASTM D-732 |
|
MPa |
| 揉曲模量 |
23℃ |
ASTM D-790 |
|
MPa |
| 1%形变时的压应力 |
--- |
ASTM D-695 |
|
MPa |
| 埃佐冲击强度 |
23℃ |
ASTM D-256 |
|
j/m |
| 拉伸冲击强度 |
长试样23℃ |
ASTM D-1822 |
|
KJ/m2 |
| 拉伸冲击强度 |
短试样23℃ |
ASTM D-1822 |
|
KJ/m2 |
| 电气性能 |
耗散因数 |
106Hz(cps) |
ASTM D-150 |
|
--- |
| 体积电阻率 |
--- |
ASTM D-257 |
|
Ω.cm |
| 介电常数 |
100Hz(cps) |
ASTM D-150 |
|
--- |
| 介电常数 |
103Hz(cps) |
ASTM D-150 |
|
--- |
| 介电常数 |
106Hz(cps) |
ASTM D-150 |
|
--- |
| 耗散因数 |
100Hz(cps) |
ASTM D-150 |
|
--- |
| 耗散因数 |
103Hz(cps) |
ASTM D-150 |
|
--- |
| 热 性 能 |
线性热膨胀系数 |
--- |
ASTM D-696 |
|
m/m/℃ |
| 导热系数 |
--- |
--- |
|
w/mk |
| UL可燃性导级 |
--- |
UL 94 |
|
--- |
| 熔点 |
Fisher Johns法 |
ASTM D-789 |
|
℃ |
| 熔点结晶 |
--- |
ASTM D-2177 |
|
℃ |
| 脆化温度 |
--- |
ASTM D-746 |
|
℃ |
| 热畸变温度 |
18×106Pa |
ASTM D-648 |
|
℃ |
| 热畸变温度 |
(0.5)×106Pa |
ASTM D-648 |
|
℃ |
| 荷重形变 |
13.8MPa，50℃ |
ASTM D-621 |
|
% |
| 其它性能 |
需氧指数 |
--- |
ASTM D-2863 |
|
% |
本公司长期供应 PA66（聚酰胺双6）塑胶原料产品
PA66 101L美国杜邦 经润滑 耐磨损 电气性能佳
PA66 101F美国杜邦 经润滑 易脱模 电气性能佳
PA66 ST801美国杜邦 超韧耐寒级 注射成型
PA66 ST801A美国杜邦 超韧耐寒级 注射成型
PA66 FE5171美国杜邦 食品级 加33%玻纤
PA66 70G33L美国杜邦 加33%玻纤 抗蠕变 注射成型
PA66 70G13L美国杜邦 加13%玻纤 注射成型
PA66 70G43L美国杜邦 加43%玻纤 抗蠕变 注射成型
PA66 80G14A美国杜邦 加14%玻纤 注射成型
PA66 80G14AHS美国杜邦 加14%玻纤 注射成型