沙伯基础创新PC LEXAN EXL1414 产品特性：耐候，耐低温-40℃，超韧性，可加工性好，脱模性能良好，延展性好，生产周期快，用于手机外壳和低温寒冷使用产品
我公司提供的产品均为正牌塑胶原料，品质保证，货源稳定，送货上门，可免费提供官方物性表、UL黄卡，并随货提供RoHS报告、SGS报告等，索取权威资料请致电13268582149
PC EXL1414 物性表：
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Molding Shrinkage - Across Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.35 | % | ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 2 | 2020 | MPa | ASTM D638 |
| Tensile Modulus | 2150 | MPa | ISO 527-2/1 |
| Tensile Strength 3 (Yield) | 55.5 | MPa | ASTM D638 |
| Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strength 3 (Break) | 50.3 | MPa | ASTM D638 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation 3 (Yield) | 6.0 | % | ASTM D638 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Tensile Elongation 3 (Break) | 98 | % | ASTM D638 |
| Tensile Strain (Break) | 120 | % | ISO 527-2/50 |
| Flexural Modulus 4 (50.0 mm Span) | 2230 | MPa | ASTM D790 |
| Flexural Modulus 5 | 2250 | MPa | ISO 178 |
| Flexural Strength 5, 6 | 85.0 | MPa | ISO 178 |
| Flexural Strength 4 (Yield, 50.0 mm Span) | 92.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
| -30°C | 65 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 770 | J/m | |
| 23°C | 870 | J/m | |
| Notched Izod Impact Strength 8 | ISO 180/1A | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Unnotched Izod Impact Strength 8 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 70.0 | J | ASTM D3763 |
| Hardness | Nominal Value | Unit | Test Method |
| Rockwell Hardness | ASTM D785 | ||
| L-Scale | 89 | ||
| R-Scale | 121 | ||
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 139 | °C | ASTM D648 |
| Heat Deflection Temperature 9 (0.45 MPa, Unannealed, 100 mm Span) | 140 | °C | ISO 75-2/Be |
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 124 | °C | ASTM D648 |
1528-8857-388