沙伯基础创新PC LEXAN BPL1000 特性：无卤阻燃(0.8mm V0)，良好的抗冲击性，高流动性(25g/10 min)，薄壁应用的理想选择，用于手机电池外壳
我公司提供的产品均为正牌塑胶原料，品质保证，货源稳定，送货上门，可免费提供官方物性表、UL黄卡，并随货提供RoHS报告、SGS报告等，索取权威资料请致电13268582149
PC BPL1000 物性表：
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 23.2 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | Internal Method | ||
| -- 2 | 0.50 to 0.70 | % | |
| 3.20 mm | 0.50 to 0.70 | % | |
| Molding Shrinkage - Across Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.35 | % | ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 3 | 2680 | MPa | ASTM D638 |
| Tensile Modulus | 2460 | MPa | ISO 527-2/1 |
| Tensile Strength 4 (Yield) | 63.4 | MPa | ASTM D638 |
| Tensile Stress (Yield) | 64.8 | MPa | ISO 527-2/50 |
| Tensile Strength 4 (Break) | 51.0 | MPa | ASTM D638 |
| Tensile Stress (Break) | 53.5 | MPa | ISO 527-2/50 |
| Tensile Elongation 4 (Yield) | 4.8 | % | ASTM D638 |
| Tensile Strain (Yield) | 4.7 | % | ISO 527-2/50 |
| Tensile Elongation 4 (Break) | 96 | % | ASTM D638 |
| Tensile Strain (Break) | 97 | % | ISO 527-2/50 |
| Flexural Modulus 5 (50.0 mm Span) | 2670 | MPa | ASTM D790 |
| Flexural Modulus 6 | 2370 | MPa | ISO 178 |
| Flexural Strength 6, 7 | 94.8 | MPa | ISO 178 |
| Flexural Strength 5 (Yield, 50.0 mm Span) | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength 8 (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 600 | J/m | ASTM D256 |
| Notched Izod Impact Strength 9 | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Instrumented Dart Impact (23°C, Total Energy) | 48.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 106 | °C | ASTM D648 |
| Heat Deflection Temperature 10 (1.8 MPa, Unannealed, 64.0 mm Span) | 96.1 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 111 | °C | ASTM D1525 11 |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ISO 306/B50 |
| -- | 114 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-40 to 40°C) | 0.000070 | cm/cm/°C | ASTM E831 |
| CLTE - Flow (-40 to 40°C) | 0.000070 | cm/cm/°C | ISO 11359-2 |
| CLTE - Transverse (-40 to 40°C) | 0.000070 | cm/cm/°C | ASTM E831 |
| CLTE - Transverse (-40 to 40°C) | 0.000070 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
| Surface Resistivity | > 1.0E+15 | ohm | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohm·cm | IEC 60093 |
| Dielectric Strength (1.60 mm, in Oil) | 27 | kV/mm | ASTM D149 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.00 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.030 | ||
| 60 Hz | 0.030 | ||
| 1 MHz | 0.010 | ||
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating - UL | UL 94 | ||
| 0.800 mm | V-0 | ||
| 0.450 mm | V-2 |