性能项目
|
测试方法
|
测试数据
|
数据单位
|
|
熔体流动速率
|
ASTM D-1238
|
1.0
|
g/10min
|
|
熔点
|
HPC
|
94
|
℃
|
|
断裂拉伸强度
|
ASTM D-638
|
21.56
|
MPa
|
|
断裂伸长率
|
ASTM D-638
|
650
|
%
|
|
肖氏硬度
|
ASTM D-2240
|
46
|
|
|
拉伸模量
|
ASTM D-638
|
40
|
MPa
|
|
落球冲击强度
|
ASTM D-1709A
|
＞400
|
g
|
|
断裂伸长率
|
ASTM D-882
|
400
|
%
|
|
维卡软化点
|
ASTM D-1525
|
85
|
℃
|
|
VA含量
|
HPC
|
9
|
wt.%
|
|
密度
|
ASTM D-1505
|
0.930
|
g/cm3
|
|
薄膜厚度
|
HPC
|
60
|
μm
|
|
雾度
|
ASTM D-1003
|
4.5
|
%
|
|
光泽度
|
ASTM D-2457
|
100
|